The Anycubic PLA Basic Filament is a dependable choice for FDM 3D printer users who want consistent, hassle-free prints in a rich bronze colour. Designed for everyday printing, it feeds smoothly through standard FDM machines to deliver clean extrusion and reliable layer adhesion across a wide range of projects. Whether you're prototyping, creating decorative pieces, or working through a backlog of functional prints, the 1kg spool gives you plenty of material to keep the printer running. A straightforward, no-fuss filament that gets the job done.

Features

• 1.75mm diameter compatible with FDM 3D printers using 1.75mm filament
• 1kg spool weight for extended print runs
• Neatly wound spool for consistent, tangle-free feeding
• Precise extrusion with bubble-free output
• PLA material a widely supported and easy-to-print filament type

Specifications

• Colour Code: Bronze (#7C4D3A)
• Consumable Type: PLA Filament
• Compatible With: FDM 3D Printers with 1.75mm filament compatibility
• Dry Out Before Use: Recommended
• Drying Condition: 45-50 , 6-8 h
• ACE Compatibility: Compatible
• Nozzle Size: Recommended 0.2 mm or above
• Printing Temperature: 190-230
• Heated Bed Temperature: 55-56
• Recommended Printing Speed: 50-200 mm/s
• Cooling Time: 8 s
• Maximum Volume Speed (Flow Rate): 12 mm³/s
• Density: 1.24 g/cm³
• Melt Index: 4~10 g/10 min (190 /2.16 kg)
• Melting Point Temperature: 166
• Vicat Softening Temperature: 55
• Heat Deflection Temperature (0.45MPa): 54
• Young's Modulus: 2534±85 Mpa
• Tensile Strength: 48±5 Mpa
• Elongation at Break: 8±1%
• Bending Modulus: 3360±100 Mpa
• Bending Strength: 90±3 MPa
• lzod lmpact Strength (X-Y): 22±2 kJ/m²
• Tensile Strength (Z): 26±1 MPa
• Product Weight: 1000g