Anycubic PLA Basic Filament 1kg – White

Reliable PLA filament for FDM printing | Neatly wound for consistent feeding | Vibrant, true-to-colour white | 1kg spool

The Anycubic PLA Basic Filament 1kg in White is a dependable everyday filament for FDM 3D printer users who want consistent, trouble-free results. Neatly wound to prevent tangles and ensure smooth, uninterrupted feeding, it delivers precise extrusion with minimal bubbling so your prints come out clean from first layer to last. The bright white colour prints true and is well-suited to models, prototypes, and functional parts alike. A solid, straightforward choice for any FDM printer running 1.75mm PLA.

Features

• 1.75mm diameter compatible with FDM 3D printers using 1.75mm filament
• 1kg spool weight for extended print runs
• Neatly wound spool for consistent, tangle-free feeding
• Precise extrusion with bubble-free output
• PLA material a widely supported and easy-to-print filament type

Specifications

• Colour Code: White (#EFF0F1)
• Consumable Type: PLA Filament
• Compatible With: FDM 3D Printers with 1.75mm filament compatibility
• Dry Out Before Use: Recommended
• Drying Condition: 45-50 , 6-8 h
• ACE Compatibility: Compatible
• Nozzle Size: Recommended 0.2 mm or above
• Printing Temperature: 190-230
• Heated Bed Temperature: 55-56
• Recommended Printing Speed: 50-200 mm/s
• Cooling Time: 8 s
• Maximum Volume Speed (Flow Rate): 12 mm³/s
• Density: 1.24 g/cm³
• Melt Index: 4~10 g/10 min (190 /2.16 kg)
• Melting Point Temperature: 166
• Vicat Softening Temperature: 55
• Heat Deflection Temperature (0.45MPa): 54
• Young's Modulus: 2534±85 Mpa
• Tensile Strength: 48±5 Mpa
• Elongation at Break: 8±1%
• Bending Modulus: 3360±100 Mpa
• Bending Strength: 90±3 MPa
• lzod lmpact Strength (X-Y): 22±2 kJ/m²
• Tensile Strength (Z): 26±1 MPa
• Product Weight: 1000g